1.2436
X210CrW12 / AISI: D6
Delivery Method : Normalized, annealed 180-220HB
Usage Areas : It is a high carbon cold work tool steel with ledeburitic structure. This material, which shows dimensional stability during the heat treatment and can harden in the air, is widely used in the cutting of silicon steel sheets, punches of various sizes, cutting dies, paper and plastic cutting knives, deep drawing and spinning dies. It has high abrasion resistance.
*Time interval varying depending on the section.
Delivery Method : Normalized, annealed 180-220HB
Usage Areas : It is a high carbon cold work tool steel with ledeburitic structure. This material, which shows dimensional stability during the heat treatment and can harden in the air, is widely used in the cutting of silicon steel sheets, punches of various sizes, cutting dies, paper and plastic cutting knives, deep drawing and spinning dies. It has high abrasion resistance.
| Chemical Composition (%) | C | Si | Mn | Cr | V |
| % Average | 2,10 | 0,25 | 0,45 | 12,00 | 0,70 |
| DIN Analysis | 2,00-2,30 | 0,10-0,40 | 0,30-0,60 | 11,00-13,00 | 0,60-0,80 |
| Thermal Conductivity ( W/ m.K ) | 20°C | 350°C | 700°C |
| 16,7 | 20,5 | 24,2 |
| HEAT TREATMENT DATA | |||
| Temperature (°C) | Time (Hours) | Cooling Environment | |
| Softening Annealing | 800-840 | 2-5* | Bake |
| Stress Relieving | 600-650 | 2* | Bake |
| Hardening | 950-980 | - | Oil, hot bath 500-550 ° C, air |
| Tempering | 150-300 | 1 hour for every 20 mm | Air |
*Time interval varying depending on the section.